Effect of delayed light-curing on solubility, color stability, and opacity of Fuji II LC glass ionomer cement: original article / Efeito da fotopolimerização tardia na solubilidade, estabilidade de cor e opacidade do cimento de ionômero de vidro Fuji II LC: artigo original

Objective: Resin-modified glass ionomer (RMGI) cements are among the commonly used restorative materials in low stress-bearing areas and also for temporary restorations. The competition between acid-base reactions and light polymerization reactions in delayed curing of RMGIs can affect their physical and mechanical properties, as well as their degree of conversion. Since solubility, color stability, and opacity are among the main physical properties affecting the durability and clinical service of RMGI restorations, this study aimed to assess the effect of delayed curing on solubility, color stability, and opacity of Fuji II LC RMGI. Material and Methods: This in vitro, experimental study evaluated 80 Fuji II LC RMGI specimens (10 specimens per each in 4 groups) in terms of solubility, color stability, and opacity at 6 months later. Specimens were cured immediately or were cured with 1, 5 and 10 min delay. Results: Maximum solubility and minimum change in opacity and color stability at 6 months were noted in the group with delayed curing by 10 min. A significant difference was noted in the solubility of specimens cured after 10 min and 1 min. Significant differences were also noted in the opacity and color stability of specimens cured after 10 min and all other groups (P < 0.05). Conclusion: Delayed curing by 1 min decreased the solubility of RMGI specimens compared with immediate curing or curing after 5 min. Although this difference did not reach statistical significance. Color stability and changes in opacity are mainly influenced by the acid-base reactions rather than polymerization reactions.(AU)

Objetivo: Cimentos de ionômero de vidro modificado por resina (CIVMR) estão entre os materiais restauradores mais comumente utilizados em áreas de baixa tensão e também para restaurações temporárias. A competição entre reações ácido-base e reações provenientes da fotopolimerização tardia dos CIVRMs podem afetar suas propriedades físicas e mecânicas, bem como seu grau de conversão. Uma vez que a solubilidade, estabilidade de cor e opacidade estão entre as principais propriedades físicas que afetam a durabilidade e o tempo de serviço clinico de restaurações de CIVMR, este estudo teve como objetivo avaliar o efeito da fotopolimerizaçao tardia na solubilidade, estabilidade de cor e opacidade do CIVMR Fuji II LC. Material e Métodos: Este estudo experimental in vitro avaliou 80 espécimes de CIVMR Fuji II LC (4 grupos com 10 espécimes cada) em termos de solubilidade, estabilidade de cor e opacidade apos 6 meses. As amostras foram fotopolimerizadas imediatamente ou com 1, 5 e 10 min de atraso. Resultados: Máxima solubilidade e mínima alteração na opacidade e estabilidade da cor em 6 meses foram observadas no grupo com fotopolimerização tardia em 10 min. Uma diferença significativa foi observada na solubilidade das amostras fotopolimerizadas após 10 min e 1 min. Diferenças significativas também foram observadas na opacidade e estabilidade de cor das amostras fotopolimerizadas após 10 min e em todos os outros grupos (P <0,05). Conclusão: A fotopolimerizaçao tardia em 1 min diminuiu a solubilidade das amostras CIVMR em comparação com a fotopolimerizaçao imediata ou após 5 min. Embora essa diferença não tenha alcançado significância estatística. A estabilidade da cor e as mudanças na opacidade são influenciadas principalmente por reações ácido-base, em vez de reações causadas pela polimerização(AU)

Influence of Cavity Dimensions on Microleakage of Two Bulk-Fill Composite Resins

Objective: To evaluate the effect of cavity dimensions on the amount of microleakage in two different types of bulk-fill composite resins. Material and Methods: Forty class II cavities were prepared in the mesial and distal surfaces of human molars without any carious lesions. The samples were divided into 4 groups (n=10): Group 1: cavities with 3 mm of buccolingual width (known as the smaller cavity), filled with Tetric N-Ceram Bulk Fill composite resin; Group 2: cavities with 6 mm of buccolingual width (larger cavity), filled with Tetric N-Ceram Bulk Fill composite resin; Group 3: cavities with 3 mm of buccolingual width, filled with X-Tra Base composite resin; and Group 4: cavities with 6 mm of buccolingual width, filled with X-Tra Base composite. After the specimens were thermocycled for 500 cycles at 5/55°C, they were immersed in 1% methylene blue for 24 hours, and then cut into sections mesiodistally in the longitudinal axis of each tooth. Then, the samples were scored regarding the amount of dye penetration in two occlusal and gingival areas under a stereomicroscope (x32). Data was submitted to Kruskal- Wallis and Mann-Whitney tests. Results: The highest degrees of microleakage in larger cavities filled with X-Tra Base among the four groups. There was a significant statistic difference (p=0.012) between large and small cavities filled with X-Tra Base (Groups 3 and 4); however, there was no significant difference between the two cavity sizes of Tetric N-Ceram Bulk-filled groups. Conclusion: Microleakage of composite resins depends on the dimension of the cavity and the type of composite resin used.

Effect of powder/liquid ratio of glass ionomer cements on flexural and shear bond strengths to dentin

Aim: This study evaluated the effect of varying the powder/liquid (P/L) ratio on the shear bond to dentin (SBS) and flexural strength (FS) of glass ionomer cements (GIC)s. Methods: Three types of GICs (Fuji II, Fuji II LCi and Fuji IX GP) were mixed using the following P/L ratios: 20% lower than the manufacturer's ratio, manufacturer's ratio, 20% higher than the manufacturer's ratio (9 groups). SBS (MPa) was evaluated and the mode of failure checked under stereomicroscope. FS (MPa), of the specimens (25×2×2mm) assessed using a universal testing machine at a crosshead speed of 1 mm/min. The data were subjected to two-way ANOVA and Tukey's test for analysis (p< 0.05). Results: The highest SBS and FS (MPa) obtained for Fuji II, Fuji II LCi and Fuji IX were 6.12±2.11 and 16.96±2.73; 11.60±3.19 and 49.58±8.75; 7.39±2.77 and 20.32±2.09, respectively. The interaction between materials and P/L ratios had no significant effect on the properties tested in this study. Fuji II LCi exhibited significantly higher SBS and FS than the other two GICs in all P/L ratios. Conclusions: No significant differences were observed between Fuji II and Fuji IX. Twenty percent variation in P/L ratio had no significant effect on SBS and FS of GICs.